標(biāo)樣編號(hào) | ATM N24017 | ATM N24013 | 78x N24004 | RSA N24001 | ATM N24006 | ATM N24019 | SUP N24006p | 58A Co-L605D | BS SG24001 |
基體 | 鈷基 | 鈷基 | 鈷基 | 鈷基 | 鈷基 | 鈷基 | 鈷基 | 鈷基 | 鈷基 |
名稱 | 鈷基合金光譜 | 鈷基合金光譜 | 鈷基合金光譜 | 鈷基合金光譜 | 鈷基合金光譜 | 鈷基合金光譜 | 鈷基合金光譜 | 鈷基合金光譜 | 鈷基合金光譜 |
Ag | - | - | - | - | - | - | - | - | - |
Al | 0.138 | 0.08 | - | <0.01 | *0.003 | 0.07 | 0.05 | 0.067 | 0.014 |
As | - | - | - | - | - | <0.0100 | - | - | 0.048 |
B | 0.001 | 0.0015 | <0.0010 | <0.0001 | *0.001 | *0.0006 | <0.05 | 0.002 | 0.0033 |
Bi | - | - | - | - | - | - | - | - | 0.0003 |
C | 0.064 | 1.06 | 0.089 | 0.126 | -0.002 | 1.02 | 0.12 | 0.1 | 0.061 |
Re | - | - | - | - | - | - | - | - | *0.12 |
Zr | <0.01 | *0.001 | - | <0.01 | 0.002 | <0.0100 | - | - | 0.0011 |
Co | 53.4 | 57.9 | 64.87 | 51.5 | 48.4 | 57 | 50.8 | 48.3 | 59.26 |
Cr | 25.4 | 29.9 | 27.12 | 20 | -0.002 | 30.7 | 20.3 | 20.4 | 0.69 |
Cu | 0.019 | 0.009 | 0.005 | 0.001 | -0.002 | 0.015 | 0.03 | 0.011 | 0.052 |
Fe | 2.99 | 0.84 | -0.93 | 1.8 | 49.6 | 2.68 | 1.1 | 2.31 | 1.18 |
La | - | - | - | - | - | - | 0.03 | - | - |
Mg | 0.0043 | *0.0002 | - | <0.001 | *0.001 | <0.0100 | <0.005 | - | <0.001 |
Mn | 0.79 | 1.47 | 0.78 | 1.58 | 0.003 | 1.48 | 1.5 | 1.86 | 0.045 |
Mo | 4.72 | 0.954 | 5.47 | - | -0.002 | 0.02 | 0.12 | 0.33 | 19.13 |
N | 0.113 | 0.0417 | 0.17 | 0.026 | 0.0004 | 0.017 | <0.05 | - | - |
Nb | 0.016 | 0.024 | - | <0.005 | 0.038 | 0.014 | <0.05 | 0.082 | 0.99 |
Ni | 9.47 | 2.99 | 0.15 | 9.78 | 0.037 | 2.59 | 10.3 | 10.7 | 2.08 |
O | 0.0012 | 0.0009 | - | - | 0.0082 | *0.001 | <0.005 | - | - |
P | 0.0064 | 0.0053 | 0.002 | 0.002 | 0.0013 | -0.004 | 0.003 | 0.009 | 0.111 |
Pb | - | *0.00001 | - | <0.0001 | - | <0.0100 | - | - | *0.0014 |
S | 0.0004 | 0.0003 | 0.002 | 0.0007 | 0.0011 | <0.0050 | 0.0009 | 0.001 | 0.014 |
Sb | - | *0.0002 | - | - | - | <0.0010 | - | - | -0.07 |
Si | 0.24 | 0.64 | 0.59 | 0.016 | 0.029 | 0.61 | 0.05 | 0.28 | 0.7 |
Sn | <0.01 | *0.0001 | - | <0.001 | <0.001 | <0.0100 | - | - | 0.008 |
Ta | 0.02 | 0.03 | - | <0.01 | *0.01 | <0.0200 | <0.05 | 0.021 | 0.28 |
Ti | 0.007 | 0.009 | - | - | *0.002 | 0.007 | 0.052 | 0.02 | 0.026 |
V | 0.02 | 0.01 | 0.005 | 0.005 | 1.94 | 0.011 | 0.013 | 0.014 | 0.3 |
W | 2.39 | 3.98 | <0.01 | 15.1 | *0.001 | 3.92 | 15.2 | 15.6 | 14.91 |